ČSN EN 15826 - Smalty - Terminologie
| Stáhnout normu: | ČSN EN 15826 (Zobrazit podrobnosti) Zákazníci, kteří mají na svém počítači sjednanou od České agentury pro standardizaci (ČAS) službu ČSN on-line pro elektronický přístup do plných textů norem v pdf (verzi pro firmy nebo pro jednotlivce), mohou zde přímo otevírat citované ČSN. |
| Datum vydání/vložení: | 2015-09-01 |
| Třidící znak: | 945000 |
| Obor: | Zkoušení ochranných vrstev |
| ICS: |
|
| Stav: | Neplatná |
- 2.1 abrasive blasting
- 2.2 abrasion resistance
- 2.3 acid resistance
- 2.4 adherence (enamel-metallic substrate) adhesion
- 2.5 adherence of powder
- 2.6 ageing
- 2.7 air sealair curtain
- 2.8 alkali degreasing
- 2.9 alkali resistance
- 2.10 aluminium enamel
- 2.11 anneal, annealing
- 2.12 anti-scale compound
- 2.13 back emissionback ionisation (electrostatic powder)
- 2.14 ball mill
- 2.15 batch smelterdiscontinuous smelter
- 2.16 bead
- 2.17 beadingrim enamelling
- 2.18 beading enamelrim enamel
- 2.19 biocide
- 2.20 bisque
- 2.21 black specks
- 2.22 blank
- 2.23 blasting
- 2.24 blister
- 2.25 bloom
- 2.26 boiling
- 2.27 bolt-hole brush
- 2.28 box furnace
- 2.29 break out
- 2.30 bubble structure
- 2.31 burn-off
- 2.32 burning bar burning point burning tool
- 2.33 button test fusion button test
- 2.34 carbon boil
- 2.35 cascading
- 2.36 cast iron enamel
- 2.37 cermetceramic-metal coating
- 2.38 chalkboard enamel blackboard enamel
- 2.39 chalky surface
- 2.40 chemical resistance
- 2.41 chipping
- 2.42 cleanability
- 2.43 cleaner
- 2.44 cleaning degreasing vapour degreasing
- 2.45 clear frit transparent frit
- 2.46 coefficient of expansion
- 2.47 cold-rolled steel
- 2.48 colour matching
- 2.49 colouring oxide
- 2.50 coloured frit
- 2.51 consistency
- 2.52 continuity of coating
- 2.53 continuous furnace
- 2.54 continuous smelter
- 2.55 conventional enamelling
- 2.56 cooling zone
- 2.57 copper enamels
- 2.58 copperheads
- 2.59 cover coat enamel
- 2.60 covering power
- 2.61 crack cracking
- 2.62 crawling curling
- 2.63 crazing
- 2.64 cross-bend test
- 2.65 cup spray gun cup-gun
- 2.66 cupping
- 2.67 curtains
- 2.68 decal transfer
- 2.69 decarburised steel zero carbon steel
- 2.70 de-beading
- 2.71 decking
- 2.72 de-enamelling
- 2.73 de-setting agent
- 2.74 delayed fish-scale
- 2.75 de-vitrification
- 2.76 dimple
- 2.77 dip weightpick-upplate weight
- 2.78 dipping (wet process)swilling (wet process)
- 2.79 dipping (dry process)
- 2.80 direct fired furnace
- 2.81 direct-on-enamelling
- 2.82 discontinuity
- 2.83 double draining
- 2.84 double-face ware
- 2.85 drain line
- 2.86 drain time
- 2.87 draining
- 2.88 dredge
- 2.89 dry millingdry grinding
- 2.90 dry process enamelling
- 2.91 dry spray
- 2.92 dry weight
- 2.93 drying crack
- 2.94 dulling
- 2.95 dust coat
- 2.96 easy-to-clean enamelETC enamel
- 2.97 edging
- 2.98 edging brush
- 2.99 eggshell
- 2.100 electrophoretic deposition
- 2.101 electrostatic dry powder application
- 2.102 electrostatic wet application
- 2.103 enamelling aluminium
- 2.104 enamelling cast iron
- 2.105 enamelling iron
- 2.106 etched
- 2.107 Faraday cage effect
- 2.108 film strength
- 2.109 fineness test
- 2.110 fire tool marksburning tool marksfire markspin markspoint marks
- 2.111 firing
- 2.112 firing range
- 2.113 firing temperaturematuring temperature
- 2.114 firing time
- 2.115 firing zone
- 2.116 fish-scale
- 2.117 flaw
- 2.118 flow button
- 2.119 flow coating
- 2.120 fluidity
- 2.121 flux
- 2.122 ford cup
- 2.123 fork
- 2.124 fritflake
- 2.125 fritting
- 2.126 fusion flow test
- 2.127 galvanic nickel dip
- 2.128 gasaturagassinggrizzlespongy enamel
- 2.129 glass
- 2.130 glass eye
- 2.131 gloss
- 2.132 graining
- 2.133 graining roller
- 2.134 grit blasting
- 2.135 ground-coat
- 2.136 hairlinesstrain-linestension-lines
- 2.137 hardness
- 2.138 hollow warecookwareovenware
- 2.139 hot dustingdredging
- 2.140 impact test
- 2.141 jar millpot mill
- 2.142 jewellers' enamel
- 2.143 lamination
- 2.144 lump
- 2.145 lustre
- 2.146 marble effect
- 2.147 matt enamel
- 2.148 mediumsqueegee oil
- 2.149 metal blister
- 2.150 mill additions
- 2.151 millscale
- 2.152 mottled waregraniteware
- 2.153 muffle furnace
- 2.154 neutraliser
- 2.155 nickel dip
- 2.156 one-coat enamelling
- 2.157 one-fire enamelling
- 2.158 opacifier
- 2.159 opaque vitreous enamel
- 2.160 orange peel
- 2.161 over-spray
- 2.162 pearl linesbubble lines
- 2.163 peeling
- 2.164 perrittscomb-rack
- 2.165 pickle basket
- 2.166 pickling
- 2.167 pigments
- 2.168 pig skinleather
- 2.169 pinholepinholingholiday
- 2.170 pit
- 2.171 plugging compoundfiller
- 2.172 pop-off
- 2.173 pore
- 2.174 porosity
- 2.175 porosity
- 2.176 pot furnace
- 2.177 powder enamel
- 2.178 powder enamelling
- 2.179 powdered enamel
- 2.180 powder-powder enamelling
- 2.181 preheat zone
- 2.182 pressure potpressure tank
- 2.183 primary boiling
- 2.184 process fish-scalepoppers
- 2.185 pyro (2.185)
- 2.186 pyrolytic enamel
- 2.187 ready-to-use-enamelRTU enamel
- 2.188 reboiling
- 2.189 re-circulating dip tank
- 2.190 reclaim enamel
- 2.191 recovery timecomeback
- 2.192 reduction nickel dipauto-catalytic nickel dipelectroless nickel dip
- 2.193 reflectance
- 2.194 reflectivity
- 2.195 refractory composite coating
- 2.196 resistivity
- 2.197 rheology
- 2.198 ripple
- 2.199 rotary smelter
- 2.200 rubbing stonerubbing down stone
- 2.201 rust inhibitor
- 2.202 sag test
- 2.203 saggingdistortionwarping
- 2.204 sagging
- 2.205 sand blasting
- 2.206 sanitary ware
- 2.207 satin finish
- 2.208 scab
- 2.209 scale
- 2.210 scaling
- 2.211 screening inkscreening pasteceramic ink
- 2.212 scumming
- 2.213 self clean enamelcontinuous clean enamelcatalytic enamel
- 2.214 self-mottled ware
- 2.215 semi-muffle
- 2.216 semi-opaque enamel
- 2.217 set
- 2.218 setting-up agentset-up salt
- 2.219 shiner scaleshiner
- 2.220 shorelines
- 2.221 silver steelsilver metal
- 2.222 sliding
- 2.223 slipslurry
- 2.224 slip gauge
- 2.225 slump test
- 2.226 slushing
- 2.227 smelt
- 2.228 smelting
- 2.229 softening temperature
- 2.230 soilability
- 2.231 solubility
- 2.232 spallspalling
- 2.233 spark test
- 2.234 spray booth
- 2.235 spray gun
- 2.236 spray-rate
- 2.237 stainability
- 2.238 star markspider
- 2.239 stippled finish
- 2.240 stoning
- 2.241 suspending agents
- 2.242 substrate
- 2.243 swab testsponge test
- 2.244 swab test
- 2.245 tearing
- 2.246 thixotropy
- 2.247 thread test
- 2.248 triangle bars
- 2.249 tube furnace
- 2.250 two coat-one fire enamelling
- 2.251 U-type furnace
- 2.252 vapour degreasing
- 2.253 vignetteshading
- 2.254 viscosity
- 2.255 vitreous enamelporcelain enamel
- 2.256 vitreous enamellingporcelain enamellingenamelling
- 2.257 whale-scale
- 2.258 water-break test
- 2.259 water markwater spotwater stain
- 2.260 water streakwater line
‹
Nahlásit chybu
2.61 crack cracking
defect caused by laminar interruptions in the fused coating running vertical to the surface
NOTE 1 Cracking can also occur at different angles.
NOTE 2 The causes are mainly the result of mechanical or thermal tensile stresses within the enamel coating.
2.61 trhlinky
vada způsobená laminárním porušením vypáleného povlaku probíhajícím svisle k povrchu
POZNÁMKA 1 Trhlinky mohou probíhat pod různými úhly.
POZNÁMKA 2 Hlavními příčinami vzniku vady jsou mechanická nebo tepelná tahová napětí uvnitř smaltového povlaku.